Screw dislocation-driven nanostructures of two-dimensional transition metallic dichalcogenides (2D TMDs) can characteristic chirality that allows outstanding uneven optical properties. One of many excellent representatives is WSe2 as it may well exhibit intriguing new dimension and shape-depended chemical and bodily properties in comparison with its bulk counterpart. Crystal development management in nanostructures with screw dislocation-driven development is central for exploiting their structure-related properties. Nonetheless, bottom-up syntheses of 2D TMDs often include ‘trial and error’ approaches. Right here we report on the rational synthesis planning and realizing for the binary system W:Se to attain chirality in nano-scale crystals by chemical vapor transport (CVT). For that goal, key parameters had been modelled based mostly on thermodynamic datasets. Thus, crystal development by CVT underneath addition of SeCl4 succeeds for bulk-WSe2 from 900 °C to 820 °C with a dwell time of 72 h, whereas right-handed spiral nanocrystals are obtained from 850 °C to 800 °C with a dwell time of 60 min. Left-handed spirals happen from 915 °C to 860 °C. Floor-fused SiO2 nanoparticles on an Si(100) substrate served as potential nucleation factors. Chirality of screwed WSe2 was investigated by circular-polarized Raman Spectroscopy and confirmed an depth enhance of the E12g mode of 29 % and 15 % for proper and left-handed spirals, respectively. Pyramid-like WSe2 analyzed by atomic drive microscopy exhibit step heights of round 10 nm. Electron backscatter diffraction sample reveal a convex curvature for WSe2 with the curvature radii decided as Rx = (270 ± 32) µm and Ry = (141 ± 9) µm, respectively.